ACRYLATE WHITE UD TC / RC18 / HD 70FXH/RC18/286415788261095

Download as pdf

Date07.05.2019 IMP
Sales CodeFXH/RC18/28
Product useProduct designed for security labeling applications when tamper-evident features are required. With its brittle face material characteristics, this white product, is difficult to remove in one piece without visible evidence of the tampering, once adhered.
Typical technical values
ProductA white, top coated, satin finish, acrylate film with low elongation at break.
Substance90g/m²ISO 536
Caliper51µmISO 534
Tensile strength MD67MPaISO 527/3
Elongation at break MD6%ISO 527max.
PrintabilitySuitable for UV flexo, UV screen and UV letterpress; other methods should be tested.
TypeClear permanent adhesive.
CompositionRadiation-cured UV-Acrylic.
Tack20N/25mmFTM 9(on glass)
Peel 180°23N/25mmFTM 1(on glass)
BackingHD 70
ProductA white transparent glassine backing paper.
Substance60g/m²ISO 536
Caliper53µmISO 534
Tensile strength MD6.6kN/mISO 1924
Tensile strength CD2.5kN/mISO 1924
Transparency50%DIN 53147
Total caliper130 µm
Minimum labelling temperature5 °C
Service temperature-20 °C to 100 °C
Shelf lifeFrom date of manufacture: 12 months, under FINAT defined storage conditions (+20-25°C and RH 40-50%). Prolonged storage at higher temperatures and/or humidity levels will shorten the shelf life.
Product InformationIt takes from several hours to days for the adhesive to develop its full tamper evident functionality.
Additional infoLabel corners should have a larger radius than normal (minimum 3mm). Matrix removal should take place directly after die-cutting to prevent adhesive "flowing" back, using large diameter roller, not a blade. Experience shows that higher machine speeds (compared to PVC White UD) are possible, with 3mm label gaps and 5mm radius corners. In general this product is suitable for manual and automatic dispensing. We recommend to validate the functionality under original conditions. The face destruction when an attempt to remove the label is made, requires a specific adhesion to the substrate and is typically of a tearing type. To assist the tearing of the face film when applied to polar surfaces, security slits should be added. We recommend considering all parameters that can influence the adhesion, namely substrate, temperature, application pressure and dwelling time.
DisclaimerThe performance of the product should always be tested in the actual application conditions. Our recommendations are based on our most current knowledge and experience. As our products are used in conditions beyond our control, we cannot assume any liability for damage caused through their use. Users of our products are solely responsible that the product is suitable for its intended application, and have determined such at their sole discretion. Users must comply with any applicable legislation and/or testing requirements for the finished article, and are responsible for bringing their products to market. This publication does not constitute any warranty, express or implied, and is intended only for the recipient and cannot therefore be transferred to any third party. We cannot assume any liability for the use of our products in conjunction with other materials. All our products are sold subject to UPM Raflatac’s general sales conditions, and you should ensure that any existing laws are observed. This publication replaces all previous versions. All information is subject to change without notice.

 Product availability

ServiceWidth (mm) / Length (m)
Small roll1000/500

 Do you know our services?


 ‭(Hidden)‬ News

 ‭(Hidden)‬ Brochures

 ‭(Hidden)‬ Related materials