|24.10.2013 ENG 824|
|PRODUCT||PET MATT WHITE TC 50 / RC 15 / HD 70 WHITE|
|Typical technical values|
|FACE||PET MATT WHITE TC 50|
|Product||White, matt top-coated polyester film.|
|Type||Permanent adhesive - specifically designed for polar surfaces (high surface energy substrates).|
|20||N/25mm||FTM 1||(20 min on glass)|
|Labelling temperature min|
|BACKING||HD 70 WHITE|
|Product||White high transparent glassine backing paper.|
|Tensile strength MD|
|Application||For use as barcode labels, name plates, warning, instruction or identification labels wherever a durable and dependable long-term solution on a high surface energy substrate is required: electronic components, domestic and industrial machines like hand-held electronics, housings, white goods, computer equipment, power tools and garden machinery. Excellent heat, chemical and UV resistance assure resilient adhesion for the lifecycle of products in a variety of challenging conditions.|
PET matt white TC 50/RC 15 offers excellent initial tack and final adhesion on polar surfaces like steel, aluminium, ABS or Polyester.
|Printability||Flexography, screen and letterpress. Special inks designed for non-absorbent materials should be used. The top-coated PET film provides excellent TTR printing results. The best durability can be reached with resin ribbons. We recommend validating the ink adhesion and durability under original conditions.|
RoHS (Directive 2002/95/EC) compliant.
|Typical values||The listed technical data are typical values and give indications about the performance of the material only. They are not intended for specification purpose.|
|Adhesive coatweight||23 g/m² (FTM 12)|
|Test method||Rate of removal||Value||Units|
|Low speed release (FTM 3)||300mm/min||6-14||cN/50mm|
|Adhesion||Due to the fact that the adhesive needs a certain time to reach its final adhesion, we recommend waiting at least 24h (better 72h) after dispensing the label to the substrate before proceeding with any performance tests.|
Test Conditions: 23ºC, 50%rH
FTM1: 180º Peel Adhesion (300 mm/min) with 72 h dwell time.
|PA6 + GF30||16.8|
|Powder coated panel||14.0|
|Chemical resistance||Test Conditions: |
Dwell time on glass plate: 24 h; 23°C 50% RH
Immersion in chemical: 4 h; 23°C 50% RH
|Chemical||Visual Appearance||Edge Penetration (mm)|
|Brake Fluid||no change||0|
|Engine Oil||no change||0|
|Distilled Water||no change||0|
|Dish Washing Agent||no change||0|
|Service temperature||Temperature resistance of label applied to glass. Other substrates should be tested under original conditions. A variety of different substrates have been already tested according to the UL specification. Please see table on the last page.|
|Test Conditions||Visual Appearance|
|+150 °C for 24h on glass||no significant change|
|-40 °C for 72h on glass||no significant change|
|Shelf life||From the date of manufacture: 2 years at +20°C and RH50%.|
Our recommendations are based on our most current knowledge and experience. As our products are used in conditions beyond our control, we cannot assume any liability for damage caused through their use. Users of our products are solely responsible that the product is suitable for its intended application, and have determined such at their sole discretion. Users must comply with any applicable legislation and/or testing requirements for the finished article, and are responsible for bringing their products to market.
This publication does not constitute any warranty, express or implied, and is intended only for the recipient and cannot therefore be transferred to any third party. We cannot assume any liability for the use of our products in conjunction with other materials.
All our products are sold subject to UPM Raflatac’s general sales conditions, and you should ensure that any existing laws are observed.
This publication replaces all previous versions. All information is subject to change without notice.