UPM Raflatac North America > Labelstock Products > Technical Product Information
Technical Product Information
Sales code: SY160T
|
| Last updated 11/2008 |
| |
| Caliper: | 5.9 mil. |
| Substance weight: | 111 lbs./ream (25 x 38") |
Face |
| PE Clear 85, Transparent, glossy (corona treated) polyethylene film. For prime labeling in applications where resistance against water, oil and/or chemicals is important. For labeling toiletries and cosmetics. . |
| Substance weight | 54 lbs./ream (25" x 38") | DIN53352 |
| Caliper | 3.3 mil. | DIN53370 |
| Tensile strength MD | 2,755 psi | DIN53455 |
| Tensile strength CD | 2,755 psi | DIN53455 |
| Elongation MD (min) | 350% | DIN53455 |
| Gloss | 85% | DIN67530/1 |
Adhesive |
| RP37, Acrylic dispersion clear permanent adhesive. Specially designed for film face materials. Excellent clarity, UV-stability and water resistance. |
| Tack min | 9 N FTM 9 | |
| Shear min | 10.0 h FTM 8 | |
| PE-looptack min | 5 N modified FTM 9 | |
| Labeling temperature min | 50°F | |
| Service temperature range | - 4°F ... 212°F | |
| |
| Limited adhesion at low temperatures. The highest end-use temperature must be separately checked together with the face material. Shelf life - From the date of manufacture 2 years at 68°F and RH 50%. |
Liner |
| 2.2 mil. High Density White, White transparent glassine liner. Specially developed to offer the best conversion properties. Good with photocell dispensing systems.. |
| Substance weight | 39 lbs./ream (24" x 36") | ISO536 |
| Caliper | 2.2 mil. | ISO534 |
| Tensile strength MD | 42 lbf/in. | ISO1924 |
| Tensile strength CD | 17 lbf/in. | ISO1924 |
| Transparency | 52% | ISO2469 |
| |
| Shelf life: Laminate with RP37 adhesive 2 years if stored at room temperature (+20°C), RH 50% in original packaging and protected from light. |
| The above are typical technical values and are given in good faith based upon our most up to date knowledge and experience. As the products are used outside our control we cannot take responsibility for any damage which may be caused using the product. |
Previous Page